S-Plastics Lexan RL6791resin is DEVELOPMENTAL. Availability based on pre/post consumer recycle feedstock. 11% glass reinforced injection molding grade. Black only.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 63 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 50 | MPa | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 6 | % | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 99 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 3200 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 106 | J/m | ASTM D 256 |
| Instrumented Impact Energy @ peak, 23°C | 27 | J | ASTM D 3763 |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 137 | °C | ASTM D 648 |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.28 | - | ASTM D 792 |
| Source GMD, last updated:12/29/1999 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 | °C |
| Drying Time | 3 - 4 | hrs |
| Drying Time (Cumulative) | 48 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 310 - 330 | °C |
| Nozzle Temperature | 305 - 325 | °C |
| Front - Zone 3 Temperature | 310 - 330 | °C |
| Middle - Zone 2 Temperature | 300 - 320 | °C |
| Rear - Zone 1 Temperature | 290 - 310 | °C |
| Mold Temperature | 80 - 115 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 40 - 70 | rpm |
| Shot to Cylinder Size | 40 - 60 | % |
| Vent Depth | 0.025 - 0.076 | mm |
| Source GMD, last updated:12/29/1999 | ||