S-Plastics Lexan RL6823 resin is DEVELOPMENTAL. ONE LOT LAB MATERIAL VALUES. Superior performance. Improved flow over standard materials at lower temperatures.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 58 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 55 | MPa | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 92 | % | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 89 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2100 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 640 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 54 | J | ASTM D 3763 |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 107 | °C | ASTM D 648 |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.18 | - | ASTM D 792 |
| Melt Flow Rate, 300°C/1.2 kgf | 38 | g/10 min | ASTM D 1238 |
| Source GMD, last updated:01/04/2000 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 105 | °C |
| Drying Time | 3 - 4 | hrs |
| Drying Time (Cumulative) | 24 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 250 - 270 | °C |
| Nozzle Temperature | 245 - 265 | °C |
| Front - Zone 3 Temperature | 250 - 270 | °C |
| Middle - Zone 2 Temperature | 240 - 260 | °C |
| Rear - Zone 1 Temperature | 225 - 250 | °C |
| Mold Temperature | 50 - 80 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 40 - 70 | rpm |
| Shot to Cylinder Size | 40 - 60 | % |
| Vent Depth | 0.025 - 0.076 | mm |
| Source GMD, last updated:01/04/2000 | ||
For more information please download the datesheet | |
 | S-Plastics Lexan Rl6823.pdf |