S-Plastics Lexan RL7234 resin is Restricted PC resin for Custom Color Sunwear Applications.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 62 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 72 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min | 6.3 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 125 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2270 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 93 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2410 | MPa | ASTM D 790 |
| Purity, particles per gram > 50 microns | 1 | - | S-Plastics Method |
| Tensile Stress, yield, 50 mm/min | 61 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 71 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 6 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 140 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2400 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 94 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2200 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 918 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 84 | J | ASTM D 3763 |
| Izod Impact, notched 80*10*4 +23°C | 74 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 14 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 88 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 19 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 150 | °C | ASTM D 1525 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 139 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 128 | °C | ASTM D 648 |
| HDT, 0.45 MPa, 6.4 mm, unannealed | 137 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 132 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 7.74E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 7.74E-05 | 1/°C | ASTM E 831 |
| Vicat Softening Temp, Rate B/50 | 143 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 144 | °C | ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 139 | °C | ISO 75/Be |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 126 | °C | ISO 75/Ae |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.19 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.7 - 0.9 | % | S-Plastics Method |
| Melt Flow Rate, 300°C/1.2 kgf | 7.8 | g/10 min | ASTM D 1238 |
| Density | 1.2 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 300°C/1.2 kg | 5 | cm³/10 min | ISO 1133 |
| Source GMD, last updated:08/26/2003 | |||
| (1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294. |
|||
| (2) Only typical data for selection purposes. Not to be used for part or tool design. | |||
| (3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions. | |||
| (4) Internal measurements according to UL standards. |
|
For more information please download the datesheet |
|
 |
S-Plastics Lexan RL7234.pdf |
|