S-Plastics Lexan RL7337resin is Low-viscosity multi-purpose PC having low levels of ionics species. Internal mold release and UV-stabilized.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 62 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 65 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min | 7 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 110 | % | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 93 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2340 | MPa | ASTM D 790 |
| Hardness, Rockwell M | 70 | - | ASTM D 785 |
| Hardness, Rockwell R | 118 | - | ASTM D 785 |
| Taber Abrasion, CS-17, 1 kg | 10 | mg/1000cy | ASTM D 1044 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 3204 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 694 | J/m | ASTM D 256 |
| Tensile Impact, Type "S" | 546 | kJ/m² | ASTM D 1822 |
| Falling Dart Impact (D 3029), 23°C | 169 | J | ASTM D 3029 |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 154 | °C | ASTM D 1525 |
| HDT, 0.45 MPa, 6.4 mm, unannealed | 137 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 132 | °C | ASTM D 648 |
| CTE, -40°C to 95°C, flow | 6.84E-05 | 1/°C | ASTM E 831 |
| Specific Heat | 1.25 | J/g-°C | ASTM C 351 |
| Thermal Conductivity | 0.19 | W/m-°C | ASTM C 177 |
| Relative Temp Index, Elec | 100 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 100 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 100 | °C | UL 746B |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.2 | - | ASTM D 792 |
| Specific Volume | 0.83 | cm³/g | ASTM D 792 |
| Density | 1.19 | g/cm³ | ASTM D 792 |
| Water Absorption, 24 hours | 0.15 | % | ASTM D 570 |
| Water Absorption, equilibrium, 23C | 0.35 | % | ASTM D 570 |
| Water Absorption, equilibrium, 100°C | 0.58 | % | ASTM D 570 |
| Mold Shrinkage, flow, 3.2 mm | 0.5 - 0.7 | % | S-Plastics Method |
| Melt Flow Rate, 300°C/1.2 kgf | 17.5 | g/10 min | ASTM D 1238 |
| OPTICAL | Value | Unit | Standard |
| Light Transmission | 88 | % | ASTM D 1003 |
| Haze | 1 | % | ASTM D 1003 |
| Refractive Index | 1.586 | - | ASTM D 542 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | >1.E+17 | Ohm-cm | ASTM D 257 |
| Dielectric Strength, in air, 3.2 mm | 14.9 | kV/mm | ASTM D 149 |
| Relative Permittivity, 50/60 Hz | 3.17 | - | ASTM D 150 |
| Relative Permittivity, 1 MHz | 2.96 | - | ASTM D 150 |
| Dissipation Factor, 50/60 Hz | 0.0009 | - | ASTM D 150 |
| Dissipation Factor, 1 MHz | 0.01 | - | ASTM D 150 |
| Hot Wire Ignition {PLC) | 4 | PLC Code | UL 746A |
| High Voltage Arc Track Rate {PLC} | 2 | PLC Code | UL 746A |
| High Ampere Arc Ign, surface {PLC} | 1 | PLC Code | UL 746A |
| Comparative Tracking Index (UL) {PLC} | 2 | PLC Code | UL 746A |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Recognized, 94HB Flame Class Rating (3) | 0.76 | mm | UL 94 |
| UV-light, water exposure/immersion | F1 | - | UL 746C |
| Source GMD, last updated:08/26/2003 | |||
| (1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294. |
|||
| (2) Only typical data for selection purposes. Not to be used for part or tool design. | |||
| (3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions. | |||
| (4) Internal measurements according to UL standards. |
|
For more information please download the datesheet |
|
 |
S-Plastics Lexan RL7337.pdf |
|