Melt Flow Rate, 300°C/1.2 Kgf: 10
Basic Infomation
Place of Origin: ——
Brand Name: S-Plastic Lexan
Certification: COA/ICP Test/Rohs/MSDS
Model Number: SLX2431D
Payment & Shipping Terms
Packaging Details: 25KG/BAG
Delivery Time: To be negotiated
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: To be negotiated
Product Description

S-Plastics Lexan SLX2431D resin is Medium viscosity PC copolymer blend with enhanced UV stabilization and added release agent. V2 rated. Available in diffusion colors.

 


Property

TYPICAL PROPERTIES (1)      
MECHANICAL Value Unit Standard
Tensile Stress, yld, Type I, 50 mm/min 65 MPa ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min 73 MPa ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min 6.4 % ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min >100 % ASTM D 638
Tensile Modulus, 5 mm/min 2360 MPa ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span 96 MPa ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span 2330 MPa ASTM D 790
Tensile Stress, yield, 50 mm/min 65 MPa ISO 527
Tensile Stress, break, 50 mm/min 70 MPa ISO 527
Tensile Strain, yield, 50 mm/min 6 % ISO 527
Tensile Strain, break, 50 mm/min >100 % ISO 527
Tensile Modulus, 1 mm/min 2300 MPa ISO 527
Flexural Stress, yield, 2 mm/min 100 MPa ISO 178
Flexural Modulus, 2 mm/min 2330 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact, notched, 23°C 425 J/m ASTM D 256
Izod Impact, notched, -30°C 100 J/m ASTM D 256
Instrumented Impact Total Energy, 23°C 80 J ASTM D 3763
Izod Impact, unnotched 80*10*3 +23°C NB kJ/m² ISO 180/1U
Izod Impact, notched 80*10*3 +23°C 65 kJ/m² ISO 180/1A
Izod Impact, notched 80*10*3 -30°C 10 kJ/m² ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm 65 kJ/m² ISO 179/1eA
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm 15 kJ/m² ISO 179/1eA
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
THERMAL Value Unit Standard
Vicat Softening Temp, Rate B/50 137 °C ASTM D 1525
HDT, 1.82 MPa, 3.2mm, unannealed 134 °C ASTM D 648
CTE, -40°C to 40°C, flow 6.3E-05 1/°C ASTM E 831
CTE, -40°C to 40°C, xflow 6.3E-05 1/°C ASTM E 831
CTE, -40°C to 40°C, flow 6.3E-05 1/°C ISO 11359-2
CTE, -40°C to 40°C, xflow 6.3E-05 1/°C ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C passes - IEC 60695-10-2
Vicat Softening Temp, Rate B/50 137 °C ISO 306
Vicat Softening Temp, Rate B/120 139 °C ISO 306
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm 131 °C ISO 75/Af
PHYSICAL Value Unit Standard
Specific Gravity 1.2 - ASTM D 792
Mold Shrinkage, flow, 3.2 mm 0.5 - 0.7 % S-Plastics Method
Melt Flow Rate, 300°C/1.2 kgf 10 g/10 min ASTM D 1238
Density 1.2 g/cm³ ISO 1183
Water Absorption, (23°C/sat) 0.35 % ISO 62
Moisture Absorption (23°C / 50% RH) 0.15 % ISO 62
Melt Volume Rate, MVR at 300°C/1.2 kg 9 cm³/10 min ISO 1133
FLAME CHARACTERISTICS Value Unit Standard
UL Compliant, 94V-2 Flame Class Rating (3)(4) 1.5 mm UL 94 by GE
Glow Wire Flammability Index 960°C, passes at 1.5 mm IEC 60695-2-12
Glow Wire Ignitability Temperature, 1.0 mm 825 °C IEC 60695-2-13
Glow Wire Ignitability Temperature, 2.0 mm 825 °C IEC 60695-2-13
Glow Wire Ignitability Temperature, 2.5 mm 825 °C IEC 60695-2-13
Glow Wire Ignitability Temperature, 3.0 mm 825 °C IEC 60695-2-13
Source GMD, last updated:01/24/2006    

Processing

Parameter    
Injection Molding Value Unit
Drying Temperature 120 °C
Drying Time 2 - 4 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 280 - 310 °C
Nozzle Temperature 270 - 290 °C
Front - Zone 3 Temperature 280 - 310 °C
Middle - Zone 2 Temperature 270 - 290 °C
Rear - Zone 1 Temperature 260 - 280 °C
Hopper Temperature 60 - 80 °C
Mold Temperature 80 - 110 °C
Source GMD, last updated:01/24/2006  

 

 


 

For more information please download the datesheet

S-Plastic Lexan SLX2431D Medium Viscosity PC Copolymer Blend With Enhanced UV Stabilization And Added Release Agent. 0  S-Plastics Lexan SLX2431D.pdf

 

Get The Latest Quotation

 

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

 

S-Plastic Lexan SLX2431D Medium Viscosity PC Copolymer Blend With Enhanced UV Stabilization And Added Release Agent. 1Click to consult and get the latest quotation within 24 hours!

 

S-Plastics lexan pc products

 

Free Talk 24hours

Recommended Products
Get in touch with us
Tel : 86-13925273675
Characters Remaining(20/3000)