S-Plastics Faradex AS002 resin is a compound based on Acrylonitrile Butadiene Styrene resin containing Stainless Steel. Added features of this
material include: Electrically Conductive, EMI/RFI Shielding.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield | 42 | MPa | ASTM D 638 |
| Tensile Stress, break | 39 | MPa | ASTM D 638 |
| Tensile Strain, yield | 2.2 | % | ASTM D 638 |
| Tensile Strain, break | 8.6 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2990 | MPa | ASTM D 638 |
| Flexural Stress | 75 | MPa | ASTM D 790 |
| Flexural Modulus | 2810 | MPa | ASTM D 790 |
| Tensile Stress, yield | 39 | MPa | ISO 527 |
| Tensile Stress, break | 37 | MPa | ISO 527 |
| Tensile Strain, yield | 2.2 | % | ISO 527 |
| Tensile Strain, break | 3.3 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2500 | MPa | ISO 527 |
| Flexural Stress | 66 | MPa | ISO 178 |
| Flexural Modulus | 2500 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 286 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 58 | J/m | ASTM D 256 |
| Instrumented Impact Energy @ peak, 23°C | 11 | J | ASTM D 3763 |
| Izod Impact, unnotched 80*10*4 +23°C | 20 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 7 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 97 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 87 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 7.92E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 7.56E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, flow | 7.8E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 9.6E-05 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 91 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 78 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.12 | g/cm³ | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 0.2 | % | ASTM D 570 |
| Mold Shrinkage, flow, 24 hrs | 18 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 27 | % | ASTM D 955 |
| Mold Shrinkage, flow, 24 hrs | 0.18 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.27 | % | ISO 294 |
| Density | 1.11 | g/cm³ | ISO 1183 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | 1.E+02 - 1.E+06 | Ohm-cm | ASTM D 257 |
| Surface Resistivity | 1.E+01 - 1.E+05 | Ohm | ASTM D 257 |
| Shielding Effectivness @ 3mm | 40 - 55 | dB | S-Plastics Method |
| Source GMD, last updated:02/27/2007 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.05 - 0.1 | % |
| Melt Temperature | 240 - 255 | °C |
| Front - Zone 3 Temperature | 255 - 265 | °C |
| Middle - Zone 2 Temperature | 230 - 245 | °C |
| Rear - Zone 1 Temperature | 210 - 220 | °C |
| Mold Temperature | 70 - 95 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:02/27/2007 | ||
With a strong sales network and strength, we have warehousing services in Guangzhou, Dongguan, Shenzhen free trade zone, Hong Kong and other four places (conventional product inventory exceeds 1000 tons). We can provide customers with rapid response, professional service and excellent products!
Other related products we recommend:
|
For more information please download the datesheet |
|
|
S-Plastics Faradex AS002.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|