S-Plastics Stat-loy 9X03508 resin is a compound based on PPO+PA66 resin containing Flame Retardant, Anti-Static. Added features of this
material include: Antistat, Flame Retardant, High Impact.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield | 53 | MPa | ASTM D 638 |
| Tensile Stress, break | 53 | MPa | ASTM D 638 |
| Tensile Strain, yield | 2.1 | % | ASTM D 638 |
| Tensile Strain, break | 2.2 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 4820 | MPa | ASTM D 638 |
| Flexural Stress | 82 | MPa | ASTM D 790 |
| Flexural Modulus | 3440 | MPa | ASTM D 790 |
| Tensile Stress, yield | 59 | MPa | ISO 527 |
| Tensile Stress, break | 58 | MPa | ISO 527 |
| Tensile Strain, yield | 2.4 | % | ISO 527 |
| Tensile Strain, break | 2.8 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 4470 | MPa | ISO 527 |
| Flexural Stress | 96 | MPa | ISO 178 |
| Flexural Modulus | 4000 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 427 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 37 | J/m | ASTM D 256 |
| Instrumented Impact Energy @ peak, 23°C | 8 | J | ASTM D 3763 |
| Multiaxial Impact | 1 | J | ISO 6603 |
| Izod Impact, unnotched 80*10*4 +23°C | 26 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 4 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 230 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 186 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 6.48E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 4.32E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, flow | 6.5E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 4.3E-05 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 218 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 179 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.31 | g/cm³ | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 0.9 | % | ASTM D 570 |
| Density | 1.31 | g/cm³ | ISO 1183 |
| ELECTRICAL | Value | Unit | Standard |
| Surface Resistivity | 1.E+03 - 1.E+05 | Ohm | ASTM D 257 |
| Source GMD, last updated:09/24/2008 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 200 - 230 | °C |
| Front - Zone 3 Temperature | 220 - 230 | °C |
| Middle - Zone 2 Temperature | 210 - 220 | °C |
| Rear - Zone 1 Temperature | 200 - 210 | °C |
| Mold Temperature | 40 - 55 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:09/24/2008 | ||
With a strong sales network and strength, we have warehousing services in Guangzhou, Dongguan, Shenzhen free trade zone, Hong Kong and other four places (conventional product inventory exceeds 1000 tons). We can provide customers with rapid response, professional service and excellent products!
Other related products we recommend:
|