S-Plastics Lexan EXL6033 resin is PC-Siloxane copolymer with good processability.Very low temp. ductility, UV-Stabilized, UL94 V1 rated in white colors only.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Taber Abrasion, CS-17, 1 kg | 10 | mg/1000cy | S-Plastics Method |
| Tensile Stress, yield, 50 mm/min | 55 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 60 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 7 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 100 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2100 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 80 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2150 | MPa | ISO 178 |
| Hardness, H358/30 | 90 | MPa | ISO 2039-1 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*3 +23°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*3 -30°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*3 +23°C | 70 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*3 -30°C | 55 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 75 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 60 | kJ/m² | ISO 179/1eA |
| Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| THERMAL | Value | Unit | Standard |
| Thermal Conductivity | 0.2 | W/m-°C | ISO 8302 |
| CTE, 23°C to 80°C, flow | 7.E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 80°C, xflow | 7.E-05 | 1/°C | ISO 11359-2 |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate B/50 | 138 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 140 | °C | ISO 306 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 131 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 122 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage on Tensile Bar, flow (2) | 0.6 - 0.8 | % | S-Plastics Method |
| Density | 1.2 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.35 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.15 | % | ISO 62 |
| Melt Volume Rate, MVR at 300°C/1.2 kg | 6 | cm³/10 min | ISO 1133 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | >1.E+15 | Ohm-cm | IEC 60093 |
| Surface Resistivity, ROA | >1.E+15 | Ohm | IEC 60093 |
| Dielectric Strength, in oil, 3.2 mm | 17 | kV/mm | IEC 60243-1 |
| Relative Permittivity, 50/60 Hz | 2.7 | - | IEC 60250 |
| Relative Permittivity, 1 MHz | 2.7 | - | IEC 60250 |
| Dissipation Factor, 50/60 Hz | 0.001 | - | IEC 60250 |
| Dissipation Factor, 1 MHz | 0.01 | - | IEC 60250 |
| Comparative Tracking Index | 175 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Recognized, 94V-1 Flame Class Rating (3) | 3 | mm | UL 94 |
| Source GMD, last updated:09/21/2004 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 | °C |
| Drying Time | 2 - 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 290 - 320 | °C |
| Nozzle Temperature | 280 - 310 | °C |
| Front - Zone 3 Temperature | 290 - 320 | °C |
| Middle - Zone 2 Temperature | 280 - 310 | °C |
| Rear - Zone 1 Temperature | 270 - 300 | °C |
| Hopper Temperature | 60 - 80 | °C |
| Mold Temperature | 80 - 120 | °C |
| Source GMD, last updated:09/21/2004 | ||
|
For more information please download the datesheet |
|
 |
S-Plastics Lexan EXL6033.pdf |
|