S-Plastics Lexan ML6342A resin is Medium flow, flame retardant polycarbonate available in clear, tints and opaque colours.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 62 | MPa | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 80 | % | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 90 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2200 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 640 | J/m | ASTM D 256 |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 122 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 132 | °C | ASTM D 648 |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.21 | - | ASTM D 792 |
| Water Absorption, 24 hours | 0.15 | % | ASTM D 570 |
| Mold Shrinkage, flow, 3.2 mm | 0.5 - 0.7 | % | S-Plastics Method |
| Melt Flow Rate, 300°C/1.2 kgf | 8.6 | g/10 min | ASTM D 1238 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Recognized, 94V-2 Flame Class Rating (3) | 1 | mm | UL 94 |
| Source GMD, last updated:06/18/1999 | |||
| Injection Molding | Value | Unit | |
| Drying Temperature | 120 | °C | |
| Drying Time | 3 - 4 | hrs | |
| Drying Time (Cumulative) | 48 | hrs | |
| Melt Temperature | 285 - 315 | °C | |
| Mold Temperature | 70 - 95 | °C | |
| Source GMD, last updated:06/18/1999 | |||
| THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES. | |||
| PLEASE CHECK WITH YOUR (LOCAL SALES OFFICE) FOR AVAILABILITY IN YOUR REGION | |||
| (1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294. |
|||
| (2) Only typical data for selection purposes. Not to be used for part or tool design. | |||
| (3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions. | |||
| (4) Internal measurements according to UL standards. | |||
|
For more information please download the datesheet |
|
 |
S-Plastics Lexan ML6342A.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|
|