S-Plastics Lexan EXRL0152 resin is a medium viscosity grade with Infra Red absorption properties. It is an excellent candidate for applications with high optical quality requirements, such as automotive glazing applications. Available in transparent solar and privacy tints, this can be custom matched to meet % transmittance requirements.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield, 50 mm/min | 65 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 70 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 6 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 120 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2350 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 90 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2300 | MPa | ISO 178 |
| THERMAL | Value | Unit | Standard |
| Thermal Conductivity | 0.2 | W/m-°C | ISO 8302 |
| CTE, 23°C to 80°C, flow | 7.E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 80°C, xflow | 7.E-05 | 1/°C | ISO 11359-2 |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate B/50 | 142 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 143 | °C | ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 136 | °C | ISO 75/Be |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 125 | °C | ISO 75/Ae |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 124 | °C | ISO 75/Af |
| Relative Temp Index, Elec | 130 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 125 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 125 | °C | UL 746B |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage on Tensile Bar, flow (2) | 0.5 - 0.7 | % | S-Plastics Method |
| Density | 1.2 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.35 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.15 | % | ISO 62 |
| Melt Volume Rate, MVR at 300°C/1.2 kg | 12 | cm³/10 min | ISO 1133 |
| OPTICAL | Value | Unit | Standard |
| Refractive Index | 1.586 | - | ISO 489 |
| ELECTRICAL | Value | Unit | Standard |
| Dielectric Strength, shorttime, 1.0mm | 15 | kV/mm | IEC 60243-1 |
| Dielectric Strength, in oil, 3.2 mm | 17 | kV/mm | IEC 60243-1 |
| Relative Permittivity, 50/60 Hz | 2.7 | - | IEC 60250 |
| Relative Permittivity, 1 MHz | 2.7 | - | IEC 60250 |
| Dissipation Factor, 50/60 Hz | 0.001 | - | IEC 60250 |
| Dissipation Factor, 1 MHz | 0.01 | - | IEC 60250 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| Glow Wire Flammability Index 850°C, passes at | 1 | mm | IEC 60695-2-12 |
| Oxygen Index (LOI) | 25 | % | ISO 4589 |
| Source GMD, last updated:10/25/2005 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 | °C |
| Drying Time | 2 - 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 280 - 310 | °C |
| Nozzle Temperature | 270 - 290 | °C |
| Front - Zone 3 Temperature | 280 - 310 | °C |
| Middle - Zone 2 Temperature | 270 - 290 | °C |
| Rear - Zone 1 Temperature | 260 - 280 | °C |
| Hopper Temperature | 60 - 80 | °C |
| Mold Temperature | 80 - 110 | °C |
| Source GMD, last updated:10/25/2005 | ||
|
For more information please download the datesheet |
|
 |
S-Plastics Lexan EXRL0152.pdf |
|