S-Plastics Lexan FXD153 resin is an Extrusion / Blow molding grade in a Diffusion effect, which is part of the VisualFX family. These effects have beendeveloped to meet increasing Aesthetic demands in the Marketplace. Color Package may affect properties, Application testing alwaysreccomended.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 62 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 66 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min | 7 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 110 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2340 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 93 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2340 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 3204 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 748 | J/m | ASTM D 256 |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 157 | °C | ASTM D 1525 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 138 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 132 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, xflow | 6.8E-05 | 1/°C | ASTM E 831 |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.2 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.5 - 0.7 | % | S-Plastics Method |
| Melt Flow Rate, 300°C/1.2 kgf | 2.5 | g/10 min | ASTM D 1238 |
| Source GMD, last updated:10/24/2003 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 | °C |
| Drying Time | 3 - 4 | hrs |
| Drying Time (Cumulative) | 48 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 320 - 345 | °C |
| Nozzle Temperature | 315 - 340 | °C |
| Front - Zone 3 Temperature | 320 - 345 | °C |
| Middle - Zone 2 Temperature | 310 - 330 | °C |
| Rear - Zone 1 Temperature | 300 - 320 | °C |
| Mold Temperature | 80 - 115 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 40 - 70 | rpm |
| Shot to Cylinder Size | 40 - 60 | % |
| Vent Depth | 0.025 - 0.076 | mm |
| Parameter | ||
| Extrusion Blow Molding | Value | Unit |
| Drying Temperature | 120 | °C |
| Drying Time | 2 - 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Minimum Moisture Content | 0.01 | % |
| Melt Temperature (Parison) | 265 - 280 | °C |
| Barrel - Zone 1 Temperature | 260 - 290 | °C |
| Barrel - Zone 2 Temperature | 260 - 290 | °C |
| Barrel - Zone 3 Temperature | 260 - 290 | °C |
| Barrel - Zone 4 Temperature | 260 - 290 | °C |
| Adapter - Zone 5 Temperature | 260 - 290 | °C |
| Mold Temperature | 60 - 100 | °C |
| Source GMD, last updated:10/24/2003 | ||
|
For more information please download the datesheet |
|
 |
S-Plastics Lexan FXD153.pdf |
|