S-Plastics Lexan FXE141Rresin isTransparent PC. ILLUMINATE special effects (fluorescent/edge glow colors). MFR 10.1. Internal mold release.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 60 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 69 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min | 6.6 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 131.5 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2160 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 87 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2310 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 854 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 77 | J | ASTM D 3763 |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 141 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 128 | °C | ASTM D 648 |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.19 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.3 - 0.5 | % | S-Plastics Method |
| Melt Flow Rate, 300°C/1.2 kgf | 10.1 | g/10 min | ASTM D 1238 |
| Source GMD, last updated:02/06/2001 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 | °C |
| Drying Time | 3 - 4 | hrs |
| Drying Time (Cumulative) | 48 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 295 - 315 | °C |
| Nozzle Temperature | 290 - 310 | °C |
| Front - Zone 3 Temperature | 295 - 315 | °C |
| Middle - Zone 2 Temperature | 280 - 305 | °C |
| Rear - Zone 1 Temperature | 270 - 295 | °C |
| Mold Temperature | 70 - 95 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 40 - 70 | rpm |
| Shot to Cylinder Size | 40 - 60 | % |
| Vent Depth | 0.025 - 0.076 | mm |
| Source GMD, last updated:02/06/2001 | ||
|
For more information please download the datesheet |
|
 |
S-Plastics Lexan FXE141R.pdf |
|