S-Plastics Lexan EXRL0685 resin is 40 MFR LEXAN High Flow Ductile Copolymer UV Stabilized
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 60 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 56 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min | 5.5 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 130 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2270 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 100 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2240 | MPa | ASTM D 790 |
| Hardness, Rockwell R | 120 | - | ASTM D 785 |
| Tensile Stress, yield, 50 mm/min | 63 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 56 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 6 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 97 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2180 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 91 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2180 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 728 | J/m | ASTM D 256 |
| Izod Impact, notched, 0°C | 699 | J/m | ASTM D 256 |
| Izod Impact, notched, -30°C | 115 | J/m | ASTM D 256 |
| Multiaxial Impact | 95 | J | ISO 6603 |
| Instrumented Impact Total Energy, 23°C | 56 | J | ASTM D 3763 |
| Izod Impact, unnotched 80*10*3 +23°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*3 -30°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*3 +23°C | 58 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*3 -30°C | 11 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 64 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 13 | kJ/m² | ISO 179/1eA |
| Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 135 | °C | ASTM D 1525 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 121 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 110 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 8.E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 8.E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, flow | 8.E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 8.E-05 | 1/°C | ISO 11359-2 |
| Ball Pressure Test, 125°C +/- 2°C | PASS | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate B/50 | 129 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 130 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 115 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.2 | - | ASTM D 792 |
| Density | 1.2 | g/cm³ | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm (5) | 0.5 - 0.7 | % | S-Plastics Method |
| Melt Flow Rate, 300°C/1.2 kgf | 40 | g/10 min | ASTM D 1238 |
| Density | 1.2 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.3 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.15 | % | ISO 62 |
| Melt Volume Rate, MVR at 300°C/1.2 kg | 38 | cm³/10 min | ISO 1133 |
| OPTICAL | Value | Unit | Standard |
| Light Transmission, 2.54 mm | 88 | % | ASTM D 1003 |
| Haze, 2.54 mm | <1 | % | ASTM D 1003 |
| Refractive Index | 1.582 | - | ASTM D 542 |
| Source GMD, last updated:2009/12/14 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 105 - 110 | °C |
| Drying Time | 3 - 4 | hrs |
| Drying Time (Cumulative) | 24 | hrs |
| Melt Temperature | 260 - 305 | °C |
| Nozzle Temperature | 255 - 300 | °C |
| Front - Zone 3 Temperature | 260 - 305 | °C |
| Middle - Zone 2 Temperature | 250 - 295 | °C |
| Rear - Zone 1 Temperature | 240 - 280 | °C |
| Mold Temperature | 50 - 80 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 35 - 75 | rpm |
| Shot to Cylinder Size | 40 - 60 | % |
| Vent Depth | 0.038 - 0.076 | mm |
| Source GMD, last updated:2009/12/14 | ||
|
For more information please download the datesheet |
|
 |
S-Plastics Lexan EXRL0685.pdf |
|