S-Plastics Thermocomp MF006S resin is LNP* Thermocomp* MF006S is a compound based on Polypropylene resin containing Glass Fiber. Added features of this material
include: Heat Stabilized
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break | 81 | MPa | ASTM D 638 |
| Tensile Strain, break | 1.8 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 14470 | MPa | ASTM D 638 |
| Flexural Stress | 131 | MPa | ASTM D 790 |
| Flexural Modulus | 6200 | MPa | ASTM D 790 |
| Tensile Stress, break | 80 | MPa | ISO 527 |
| Tensile Strain, break | 3 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 9120 | MPa | ISO 527 |
| Flexural Stress | 135 | MPa | ISO 178 |
| Flexural Modulus | 6800 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 603 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 53 | J/m | ASTM D 256 |
| Izod Impact, unnotched 80*10*4 +23°C | 37 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 157 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 133 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 6.84E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 4.5E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, flow | 6.9E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 4.4E-05 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 161 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 141 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.12 | g/cm³ | ASTM D 792 |
| Mold Shrinkage, flow, 24 hrs | 0.6 - 0.8 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 0.9 - 1.1 | % | ASTM D 955 |
| Mold Shrinkage, flow, 24 hrs | 0.65 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.98 | % | ISO 294 |
| Density | 1.12 | g/cm³ | ISO 1183 |
| Source GMD, last updated:09/24/2008 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Melt Temperature | 225 - 250 | °C |
| Front - Zone 3 Temperature | 240 - 250 | °C |
| Middle - Zone 2 Temperature | 215 - 225 | °C |
| Rear - Zone 1 Temperature | 195 - 205 | °C |
| Mold Temperature | 30 - 50 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:09/24/2008 | ||
Other related products we recommend:
|
For more information please download the datesheet |
|
 |