S-Plastics Thermocomp MF006SXP resin is a compound based on Polypropylene resin containing Glass Fiber. Added features of this material
include: Chemically Coupled.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break | 88 | MPa | ASTM D 638 |
| Tensile Strain, break | 3 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 7300 | MPa | ASTM D 638 |
| Flexural Stress | 139 | MPa | ASTM D 790 |
| Flexural Modulus | 6200 | MPa | ASTM D 790 |
| Tensile Stress, break | 91 | MPa | ISO 527 |
| Tensile Strain, break | 3.2 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 7600 | MPa | ISO 527 |
| Flexural Stress | 159 | MPa | ISO 178 |
| Flexural Modulus | 8700 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 704 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 117 | J/m | ASTM D 256 |
| Instrumented Impact Energy @ peak, 23°C | 3 | J | ASTM D 3763 |
| Multiaxial Impact | 2 | J | ISO 6603 |
| Izod Impact, unnotched 80*10*4 +23°C | 45 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 11 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 160 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 150 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 2.64E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 5.97E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, flow | 2.64E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 5.98E-05 | 1/°C | ISO 11359-2 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 152 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.134 | g/cm³ | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 0.02 | % | ASTM D 570 |
| Mold Shrinkage, flow, 24 hrs | 0.5 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 1 | % | ASTM D 955 |
| Mold Shrinkage, flow, 24 hrs | 0.5 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.96 | % | ISO 294 |
| Density | 1.13 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C / 50% RH) | 0.03 | % | ISO 62 |
| Source GMD, last updated:10/02/2004 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Melt Temperature | 225 - 250 | °C |
| Front - Zone 3 Temperature | 240 - 250 | °C |
| Middle - Zone 2 Temperature | 215 - 225 | °C |
| Rear - Zone 1 Temperature | 195 - 205 | °C |
| Mold Temperature | 30 - 50 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:10/02/2004 | ||
Other related products we recommend:
|
For more information please download the datesheet |
|
 |
S-Plastics Thermocomp MF006SXP.pdf |
|