S-Plastics Thermocomp MF008S resin is a compound based on Polypropylene resin containing Glass Fiber. Added features of this material
include: Chemically Coupled.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break | 86 | MPa | ASTM D 638 |
| Tensile Strain, break | 3 | % | ASTM D 638 |
| Flexural Stress | 137 | MPa | ASTM D 790 |
| Flexural Modulus | 7440 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 587 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 85 | J/m | ASTM D 256 |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 142 | °C | ASTM D 648 |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.22 | g/cm³ | ASTM D 792 |
| Mold Shrinkage, flow, 24 hrs | 0.3 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 1 | % | ASTM D 955 |
| Source GMD, last updated:10/02/2004 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Melt Temperature | 225 - 250 | °C |
| Front - Zone 3 Temperature | 240 - 250 | °C |
| Middle - Zone 2 Temperature | 215 - 225 | °C |
| Rear - Zone 1 Temperature | 195 - 205 | °C |
| Mold Temperature | 30 - 50 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:10/02/2004 | ||