S-Plastics Thermocomp MFK42AS resinis a compound based on PP resin containing Glass Fiber, Mineral.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield, 5 mm/min | 47 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 45 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 2.3 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 5000 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 74 | MPa | ISO 178 |
| Flexural Stress, break, 2 mm/min | 37 | MPa | ISO 178 |
| Flexural Strain, break, 2 mm/min | 5.4 | % | ISO 178 |
| Flexural Modulus, 2 mm/min | 4800 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | 15 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| CTE, 23°C to 60°C, flow | 5.1E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, xflow | 1.16E-04 | 1/°C | ISO 11359-2 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 99 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage, flow | 0.5 | % | S-Plastics Method |
| Density | 1.14 | g/cm³ | ISO 1183 |
| Water Absorption, 23°C/24hrs | 0.02 | % | ISO 62-1 |
| Source GMD, last updated:12/16/2008 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Melt Temperature | 225 - 250 | °C |
| Front - Zone 3 Temperature | 240 - 250 | °C |
| Middle - Zone 2 Temperature | 215 - 225 | °C |
| Rear - Zone 1 Temperature | 195 - 205 | °C |
| Mold Temperature | 30 - 50 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:12/16/2008 | ||
Other related products we recommend:
|
For more information please download the datesheet |
|
 |
S-Plastics Thermocomp MFK42AS.pdf |
|