S-Plastics Thermocomp MH0400A resin is a compound based on Polypropylene resin. Added features of this material include: High Specific
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield | 16 | MPa | ISO 527 |
| Tensile Stress, break | 15 | MPa | ISO 527 |
| Tensile Strain, yield | 1.8 | % | ISO 527 |
| Tensile Strain, break | 2.6 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 6590 | MPa | ISO 527 |
| Flexural Stress | 36 | MPa | ISO 178 |
| Flexural Modulus | 9580 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Multiaxial Impact | 2 | J | ISO 6603 |
| Izod Impact, unnotched 80*10*4 +23°C | 8 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 6 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 91 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage, flow, 24 hrs | 0.89 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 1.01 | % | ISO 294 |
| Density | 4 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C / 50% RH) | 0 | % | ISO 62 |
| Source GMD, last updated:10/01/2004 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Melt Temperature | 210 - 225 | °C |
| Front - Zone 3 Temperature | 215 - 225 | °C |
| Middle - Zone 2 Temperature | 205 - 215 | °C |
| Rear - Zone 1 Temperature | 195 - 205 | °C |
| Mold Temperature | 25 - 50 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:10/01/2004 | ||
Other related products we recommend:
|
For more information please download the datesheet |
|
 |
S-Plastics Thermocomp MH0400A.pdf |
|