S-Plastics Thermocomp PX94085 resin is a compound based on PA6 resin, containing Glass Fiber.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break, 5 mm/min | 212 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 3.4 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 14400 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 309 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 12600 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | 95 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 16 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 206 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage, flow | 0.25 | % | S-Plastics Method |
| Density | 1.55 | g/cm³ | ISO 1183 |
| Water Absorption, 23°C/24hrs | 0.4 | % | ISO 62-1 |
| Source GMD, last updated:04/07/2008 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.15 - 0.25 | % |
| Melt Temperature | 265 - 275 | °C |
| Front - Zone 3 Temperature | 275 - 290 | °C |
| Middle - Zone 2 Temperature | 265 - 275 | °C |
| Rear - Zone 1 Temperature | 250 - 260 | °C |
| Mold Temperature | 80 - 95 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:04/07/2008 | ||
Other related products we recommend:
|
For more information please download the datesheet |
|
 |
S-Plastics Thermocomp PX94085.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|