S-Plastics Thermocomp NF0061 resin is a compound based on PC+ABS resin containing Glass Fiber, Flame Retardant. Added features include
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break, 5 mm/min | 124 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 1.9 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 7800 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 161 | MPa | ISO 178 |
| Flexural Stress, break, 2 mm/min | 159 | MPa | ISO 178 |
| Flexural Strain, break, 2 mm/min | 2.5 | % | ISO 178 |
| Flexural Modulus, 2 mm/min | 7200 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | 30 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 7 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| CTE, 23°C to 60°C, flow | 3.2E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, xflow | 6.7E-05 | 1/°C | ISO 11359-2 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 114 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage, flow | 0.15 | % | S-Plastics Method |
| Density | 1.48 | g/cm³ | ISO 1183 |
| Water Absorption, 23°C/24hrs | 0.12 | % | ISO 62-1 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Compliant, 94V-0 Flame Class Rating (3)(4) | 1.6 | mm | UL 94 by GE |
| Source GMD, last updated:06/25/2008 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 200 - 230 | °C |
| Front - Zone 3 Temperature | 220 - 230 | °C |
| Middle - Zone 2 Temperature | 210 - 220 | °C |
| Rear - Zone 1 Temperature | 200 - 210 | °C |
| Mold Temperature | 40 - 55 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:06/25/2008 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Thermocomp NF0061.pdf |
|