S-Plastics Thermocomp RFZ22S resin is a compound based on Nylon 66 resin containing Glass Fiber, Milled Glass. Added features of this materialinclude: Heat Stabilized.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break | 115 | MPa | ASTM D 638 |
| Tensile Strain, yield | 2.8 | % | ASTM D 638 |
| Tensile Strain, break | 3.6 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 6460 | MPa | ASTM D 638 |
| Flexural Stress | 179 | MPa | ASTM D 790 |
| Flexural Modulus | 5300 | MPa | ASTM D 790 |
| Tensile Stress, break | 117 | MPa | ISO 527 |
| Tensile Modulus, 1 mm/min | 6430 | MPa | ISO 527 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 451 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 32 | J/m | ASTM D 256 |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 241 | °C | ASTM D 648 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 258 | °C | ISO 75/Bf |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.29 | g/cm³ | ASTM D 792 |
| Mold Shrinkage, flow, 24 hrs | 0.5 | % | ASTM D 955 |
| Source GMD, last updated:05/23/2006 | |||
| (1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294. |
|||
| (2) Only typical data for selection purposes. Not to be used for part or tool design. | |||
| (3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions. | |||
| (4) Internal measurements according to UL standards. |
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Thermocomp RFZ22S.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|