S-Plastics Thermocomp RX06324 resin is This material is Mineral filled Nylon grade with high dielectric constant
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 0 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 72 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 0 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 1.9 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 5120 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 120 | MPa | ASTM D 790 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 120 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 4440 | MPa | ASTM D 790 |
| Tensile Stress, yield, 5 mm/min | 0 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 74 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 0 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 1.8 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 5230 | MPa | ISO 527 |
| Flexural Modulus, 2 mm/min | 5010 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 352 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 37 | J/m | ASTM D 256 |
| Izod Impact, unnotched 80*10*4 +23°C | 23 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 4 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 95 | °C | ASTM D 648 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 94 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 2.19 | g/cm³ | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 2 | % | ASTM D 570 |
| Mold Shrinkage, flow, 24 hrs | 1.28 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 1.08 | % | ASTM D 955 |
| Density | 2.19 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 270°C/1.2 kg | 17 | cm³/10 min | ISO 1133 |
| ELECTRICAL | Value | Unit | Standard |
| Dissipation Factor, 900MHz | 0.011 | - | ASTM D 150 |
| Relative Permittivity, 900MHz | 7.9 | - | ASTM D 2520 - Mth B |
| Source GMD, last updated:2007/06/28 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 85 | °C |
| Drying Time | 8 - 10 | hrs |
| Melt Temperature | 260 - 270 | °C |
| Nozzle Temperature | 265 - 275 | °C |
| Front - Zone 3 Temperature | 265 - 270 | °C |
| Middle - Zone 2 Temperature | 265 - 270 | °C |
| Rear - Zone 1 Temperature | 255 - 260 | °C |
| Mold Temperature | 90 | °C |
| Back Pressure | 7 - 8 | MPa |
| Screw Speed | 110 - 130 | rpm |
| Source GMD, last updated:2007/06/28 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Thermocomp RX06324.pdf |
|