S-Plastics Thermocomp UC008H resin is a compound based on Polyphthalamide resin containing Carbon Fiber. Added features of this materialinclude: Electrically Conductive.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break | 261 | MPa | ASTM D 638 |
| Tensile Strain, break | 1 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 33780 | MPa | ASTM D 638 |
| Flexural Stress | 441 | MPa | ASTM D 790 |
| Flexural Modulus | 26820 | MPa | ASTM D 790 |
| Tensile Stress, break | 232 | MPa | ISO 527 |
| Tensile Strain, break | 1.3 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 35530 | MPa | ISO 527 |
| Flexural Stress | 425 | MPa | ISO 178 |
| Flexural Modulus | 26590 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 328 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 58 | J/m | ASTM D 256 |
| Instrumented Impact Energy @ peak, 23°C | 7 | J | ASTM D 3763 |
| Multiaxial Impact | 5 | J | ISO 6603 |
| Izod Impact, unnotched 80*10*4 +23°C | 45 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 7 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | >248 | °C | ASTM D 648 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | >250 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.38 | g/cm³ | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 0.4 | % | ASTM D 570 |
| Mold Shrinkage, flow, 24 hrs | 0.7 - 0.9 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 0.7 - 0.9 | % | ASTM D 955 |
| Mold Shrinkage, flow, 24 hrs | 0.7 - 0.9 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.7 - 0.9 | % | ISO 294 |
| Moisture Absorption (23°C / 50% RH) | 0.46 - 1.38 | % | ISO 62 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | 1.E+02 - 1.E+04 | Ohm-cm | ASTM D 257 |
| Surface Resistivity | 1.E+02 - 1.E+04 | Ohm | ASTM D 257 |
| Source GMD, last updated:04/26/2005 | |||
| (1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294. |
| (2) Only typical data for selection purposes. Not to be used for part or tool design. |
| (3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| (4) Internal measurements according to UL standards. |
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Thermocomp UC008H.pdf |
|