S-Plastics Thermocomp LC008EXP resin is a compound based on Polyketone containing Carbon Fiber. Added features include
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break, 5 mm/min | 256 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 1.6 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 26200 | MPa | ISO 527 |
| Flexural Stress, break, 2 mm/min | 341 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 22900 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | 45 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 9 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| CTE, 23°C to 60°C, flow | 4.E-06 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, xflow | 4.1E-05 | 1/°C | ISO 11359-2 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | >300 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.45 | g/cm³ | ISO 1183 |
| Source GMD, last updated:11/29/2007 | |||
| Injection Molding | Value | Unit | |
| Drying Temperature | 120 - 150 | °C | |
| Drying Time | 4 | hrs | |
| Maximum Moisture Content | 0.1 | % | |
| Melt Temperature | 380 - 390 | °C | |
| Front - Zone 3 Temperature | 380 - 395 | °C | |
| Middle - Zone 2 Temperature | 365 - 375 | °C | |
| Rear - Zone 1 Temperature | 350 - 360 | °C | |
| Mold Temperature | 140 - 165 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw Speed | 60 - 100 | rpm | |
| Source GMD, last updated:11/29/2007 | |||
| THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES. | |||
| PLEASE CHECK WITH YOUR (LOCAL SALES OFFICE) FOR AVAILABILITY IN YOUR REGION | |||
| (1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded |
|||
| samples. All samples tested under ISO test standards are prepared according to ISO 294. | |||
| (2) Only typical data for selection purposes. Not to be used for part or tool design. | |||
| (3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions. | |||
| (4) Internal measurements according to UL standards. | |||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Thermocomp LC008EXP.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|