S-Plastics Thermocomp UF006AS resin is a compound based on Polyphthalamide resin containing Glass Fiber. Added features of this materialinclude: Heat Stabilized.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break | 182 | MPa | ASTM D 638 |
| Tensile Strain, break | 1.9 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 11600 | MPa | ASTM D 638 |
| Flexural Stress | 254 | MPa | ASTM D 790 |
| Flexural Modulus | 11530 | MPa | ASTM D 790 |
| Tensile Stress, break | 167 | MPa | ISO 527 |
| Tensile Strain, break | 1.6 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 14790 | MPa | ISO 527 |
| Flexural Stress | 255 | MPa | ISO 178 |
| Flexural Modulus | 11220 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 411 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 69 | J/m | ASTM D 256 |
| Instrumented Impact Energy @ peak, 23°C | 9 | J | ASTM D 3763 |
| Multiaxial Impact | 1 | J | ISO 6603 |
| Izod Impact, unnotched 80*10*4 +23°C | 30 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 7 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 282 | °C | ASTM D 648 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 260 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.454 | g/cm³ | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 0.22 | % | ASTM D 570 |
| Mold Shrinkage, flow, 24 hrs | 0.2 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 1 | % | ASTM D 955 |
| Mold Shrinkage, flow, 24 hrs | 0.24 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.97 | % | ISO 294 |
| Density | 1.45 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C / 50% RH) | 0.41 | % | ISO 62 |
| Source GMD, last updated:10/02/2004 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 - 150 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.15 - 0.15 | % |
| Melt Temperature | 315 - 330 | °C |
| Front - Zone 3 Temperature | 325 - 340 | °C |
| Middle - Zone 2 Temperature | 315 - 325 | °C |
| Rear - Zone 1 Temperature | 310 - 320 | °C |
| Mold Temperature | 140 - 165 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:10/02/2004 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Thermocomp UF006AS.pdf |
|