S-Plastics Thermocomp QF007 resin is a compound based on Nylon 6/10 resin containing Glass Fiber.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break | 176 | MPa | ASTM D 638 |
| Flexural Stress | 268 | MPa | ASTM D 790 |
| Flexural Modulus | 8900 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 138 | J/m | ASTM D 256 |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.34 | g/cm³ | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 0.2 | % | ASTM D 570 |
| Source GMD, last updated:09/24/2008 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.12 - 0.2 | % |
| Melt Temperature | 270 - 275 | °C |
| Front - Zone 3 Temperature | 270 - 280 | °C |
| Middle - Zone 2 Temperature | 260 - 270 | °C |
| Rear - Zone 1 Temperature | 250 - 260 | °C |
| Mold Temperature | 80 - 95 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:09/24/2008 | ||