S-Plastics Thermocomp QF008S resin is a compound based on Nylon 6/10 resin containing Glass Fiber. Added features of this material include:
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break | 171 | MPa | ASTM D 638 |
| Tensile Strain, break | 3.3 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 12420 | MPa | ASTM D 638 |
| Flexural Stress | 255 | MPa | ASTM D 790 |
| Flexural Modulus | 10790 | MPa | ASTM D 790 |
| Tensile Stress, break | 183 | MPa | ISO 527 |
| Flexural Modulus | 10780 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 1110 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 133 | J/m | ASTM D 256 |
| Izod Impact, notched 80*10*4 +23°C | 15 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 219 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 207 | °C | ASTM D 648 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 214 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.41 | g/cm³ | ASTM D 792 |
| Density | 1.42 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C / 50% RH) | 0.09 | % | ISO 62 |
| Source GMD, last updated:12/17/2004 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.12 - 0.2 | % |
| Melt Temperature | 270 - 275 | °C |
| Front - Zone 3 Temperature | 270 - 280 | °C |
| Middle - Zone 2 Temperature | 260 - 270 | °C |
| Rear - Zone 1 Temperature | 250 - 260 | °C |
| Mold Temperature | 80 - 95 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:12/17/2004 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Thermocomp QF008S.pdf |
|