S-Plastics Thermocomp MF0044E resin is a compound based on Polypropylene resin containing Glass Fiber, Flame Retardant. Added features
include: Non-Halogen Flame Retardant, Easy Molding.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield, 5 mm/min | 60 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 3.9 | % | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 80 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 4600 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | 30 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 9 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 132 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage, flow (5) | 0.3 - 0.5 | % | S-Plastics Method |
| Density | 1.16 | g/cm³ | ISO 1183 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Compliant, 94V-0 Flame Class Rating (3)(4) | 1.6 | mm | UL 94 by GE |
| Source GMD, last updated:2010/06/16 | |||
| Injection Molding | Value | Unit | |
| Drying Temperature | 80 | °C | |
| Drying Time | 2 - 4 | hrs | |
| Melt Temperature | 190 - 240 | °C | |
| Front - Zone 3 Temperature | 190 - 240 | °C | |
| Middle - Zone 2 Temperature | 190 - 230 | °C | |
| Rear - Zone 1 Temperature | 190 - 230 | °C | |
| Mold Temperature | 40 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 25 - 50 | rpm | |
| Source GMD, last updated:2010/06/16 | |||
| THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES. | |||
| PLEASE CHECK WITH YOUR (LOCAL SALES OFFICE) FOR AVAILABILITY IN YOUR REGION | |||
| (1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294. |
|||
| (2) Only typical data for selection purposes. Not to be used for part or tool design. | |||
| (3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions. | |||
| (4) Internal measurements according to UL standards. | |||
| (5) Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article. |
|||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Thermocomp MF0044E.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|