S-Plastics Thermocomp RF0049S resin is a compound based on Nylon 66 resin containing Flame Retardant, Glass Fiber. Added features of this material include: Flame Retardant.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break | 136 | MPa | ASTM D 638 |
| Tensile Strain, break | 3.3 | % | ASTM D 638 |
| Flexural Stress | 199 | MPa | ASTM D 790 |
| Flexural Modulus | 7510 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 678 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 85 | J/m | ASTM D 256 |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.53 | g/cm³ | ASTM D 792 |
| Mold Shrinkage, flow, 24 hrs | 0.3 - 0.5 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 1 - 1.2 | % | ASTM D 955 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Compliant, 94V-0 Flame Class Rating (3)(4) | 1.69 | mm | UL 94 by GE |
| Source GMD, last updated:10/13/2005 | |||
| THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES. | |||
| PLEASE CHECK WITH YOUR (LOCAL SALES OFFICE) FOR AVAILABILITY IN YOUR REGION | |||
| (1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294. |
|||
| (2) Only typical data for selection purposes. Not to be used for part or tool design. | |||
| (3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions. | |||
| (4) Internal measurements according to UL standards. | |||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Thermocomp RF0049S.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|