S-Plastics Thermocomp UF008H resin is a compound based on Polyphthalamide resin containing Glass Fiber.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break | 236 | MPa | ASTM D 638 |
| Tensile Strain, break | 2.1 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 16130 | MPa | ASTM D 638 |
| Flexural Stress | 311 | MPa | ASTM D 790 |
| Flexural Modulus | 13440 | MPa | ASTM D 790 |
| Tensile Stress, break | 205 | MPa | ISO 527 |
| Tensile Strain, break | 2 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 14340 | MPa | ISO 527 |
| Flexural Stress | 321 | MPa | ISO 178 |
| Flexural Modulus | 13800 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 870 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 85 | J/m | ASTM D 256 |
| Instrumented Impact Energy @ peak, 23°C | 5 | J | ASTM D 3763 |
| Multiaxial Impact | 2 | J | ISO 6603 |
| Izod Impact, unnotched 80*10*4 +23°C | 51 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 9 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 281 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 2.34E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 2.88E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, flow | 2.48E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 3.01E-05 | 1/°C | ISO 11359-2 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 272 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.55 | g/cm³ | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 0.27 | % | ASTM D 570 |
| Mold Shrinkage, flow, 24 hrs | 0.3 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 1.2 | % | ASTM D 955 |
| Mold Shrinkage, flow, 24 hrs | 0.27 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 1.23 | % | ISO 294 |
| Density | 1.54 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C / 50% RH) | 0.42 | % | ISO 62 |
| Source GMD, last updated:10/02/2004 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 - 150 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.15 - 0.15 | % |
| Melt Temperature | 315 - 330 | °C |
| Front - Zone 3 Temperature | 325 - 340 | °C |
| Middle - Zone 2 Temperature | 315 - 325 | °C |
| Rear - Zone 1 Temperature | 310 - 320 | °C |
| Mold Temperature | 140 - 165 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:10/02/2004 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Thermocomp UF008H.pdf |
|