S-Plastics Thermocomp UFW49RS resin isa compound based on Polyphthalamide resin containing Glass Fiber, Mineral. Added features of thismaterial include: Heat Stabilized.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield, 5 mm/min | 186 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 1.1 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 20800 | MPa | ISO 527 |
| Flexural Stress, break, 2 mm/min | 278 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 18100 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | 40 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 7 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| CTE, 23°C to 60°C, flow | 1.6E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, xflow | 3.6E-05 | 1/°C | ISO 11359-2 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 251 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage on Tensile Bar, flow (2) | 0.1 - 0.3 | % | S-Plastics Method |
| Density | 1.87 | g/cm³ | ISO 1183 |
| Source GMD, last updated:12/12/2006 | |||
| (1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294. |
|||
| (2) Only typical data for selection purposes. Not to be used for part or tool design. | |||
| (3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions. | |||
| (4) Internal measurements according to UL standards. |
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Thermocomp UFW49RS.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|