S-Plastics Thermocomp RF004 resin is a compound based on Nylon 6/6 containing Glass Fiber. Characteristics of this grade are: Healthcare.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, brk, Type I, 5 mm/min | 156 | MPa | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 3.6 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 7170 | MPa | ASTM D 638 |
| Flexural Stress | 230 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 5860 | MPa | ASTM D 790 |
| Tensile Stress, break, 5 mm/min | 159 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 3.7 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 7300 | MPa | ISO 527 |
| Flexural Stress | 241 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 7000 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 833 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 101 | J/m | ASTM D 256 |
| Instrumented Impact Energy @ peak, 23°C | 11 | J | ASTM D 3763 |
| Multiaxial Impact | 2 | J | ISO 6603 |
| Izod Impact, unnotched 80*10*4 +23°C | 56 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 8 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 260 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 247 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 3.78E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 7.92E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, flow | 3.88E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, flow | 7.94E-05 | 1/°C | ISO 11359-2 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 221 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.3 | - | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 0.89 | % | ASTM D 570 |
| Mold Shrinkage, flow, 24 hrs (5) | 0.4 - 0.6 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs (5) | 1 - 3 | % | ASTM D 955 |
| Density | 1.29 | g/cm³ | ISO 1183 |
| Source GMD, last updated:2009/07/29 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.15 - 0.25 | % |
| Melt Temperature | 280 - 305 | °C |
| Front - Zone 3 Temperature | 295 - 305 | °C |
| Middle - Zone 2 Temperature | 280 - 295 | °C |
| Rear - Zone 1 Temperature | 265 - 275 | °C |
| Mold Temperature | 95 - 110 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:2009/07/29 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Thermocomp RF004.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|