S-Plastics Thermocomp RF0067K resin is a compound based on Nylon 66 resin containing Glass Fiber, Flame Retardant.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break, 5 mm/min | 110 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 1.8 | % | ISO 527 |
| Flexural Stress, break, 2 mm/min | 141 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 8200 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | 30 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 7 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 197 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage on Tensile Bar, flow (2) (5) | 0.2 - 0.4 | % | S-Plastics Method |
| Density | 1.45 | g/cm³ | ISO 1183 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Recognized, 94V-0 Flame Class Rating (3) | 0.8 | mm | UL 94 |
| Glow Wire Flammability Index 960°C, passes at | 1.5 | mm | IEC 60695-2-12 |
| Source GMD, last updated:2006/12/13 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.2 | % |
| Melt Temperature | 270 - 290 | °C |
| Front - Zone 3 Temperature | 280 - 290 | °C |
| Middle - Zone 2 Temperature | 265 - 285 | °C |
| Rear - Zone 1 Temperature | 260 - 280 | °C |
| Mold Temperature | 60 - 90 | °C |
| Back Pressure | >1 | MPa |
| Screw Speed | 80 - 120 | rpm |
| Source GMD, last updated:2006/12/13 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Thermocomp RF0067K.pdf |
|