S-Plastics Thermocomp AF002 resin is a compound based on Acrylonitrile Butadiene Styrene resin containing Glass Fiber.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break | 66 | MPa | ASTM D 638 |
| Tensile Strain, break | 2.5 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 4130 | MPa | ASTM D 638 |
| Flexural Stress | 105 | MPa | ASTM D 790 |
| Flexural Modulus | 4200 | MPa | ASTM D 790 |
| Tensile Stress, break | 64 | MPa | ISO 527 |
| Tensile Strain, break | 2.7 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 4200 | MPa | ISO 527 |
| Flexural Stress | 107 | MPa | ISO 178 |
| Flexural Modulus | 4500 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 320 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 80 | J/m | ASTM D 256 |
| Instrumented Impact Energy @ peak, 23°C | 15 | J | ASTM D 3763 |
| Multiaxial Impact | 3 | J | ISO 6603 |
| Izod Impact, unnotched 80*10*4 +23°C | 24 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 9 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 101 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 92 | °C | ASTM D 648 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 95 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.111 | g/cm³ | ASTM D 792 |
| Mold Shrinkage, flow, 24 hrs | 0.4 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 0.4 | % | ASTM D 955 |
| Mold Shrinkage, flow, 24 hrs | 0.41 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.38 | % | ISO 294 |
| Density | 1.1 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C / 50% RH) | 0.38 | % | ISO 62 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Compliant, 94HB Flame Class Rating (3)(4) | 1.5 | mm | UL 94 by GE |
| Source GMD, last updated:10/01/2004 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.05 - 0.1 | % |
| Melt Temperature | 260 | °C |
| Front - Zone 3 Temperature | 265 - 275 | °C |
| Middle - Zone 2 Temperature | 230 - 245 | °C |
| Rear - Zone 1 Temperature | 205 - 215 | °C |
| Mold Temperature | 70 - 80 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:10/01/2004 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Thermocomp AF002.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|