S-Plastics Thermocomp RF0069S resin is a compound based on Nylon 66 resin containing Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break | 165 | MPa | ASTM D 638 |
| Tensile Strain, break | 2.7 | % | ASTM D 638 |
| Flexural Stress | 240 | MPa | ASTM D 790 |
| Flexural Modulus | 12200 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 694 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 74 | J/m | ASTM D 256 |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.71 | g/cm³ | ASTM D 792 |
| Mold Shrinkage, flow, 24 hrs | 0.3 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 1 | % | ASTM D 955 |
| Source GMD, last updated:10/02/2004 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.15 - 0.25 | % |
| Melt Temperature | 275 - 290 | °C |
| Front - Zone 3 Temperature | 295 - 305 | °C |
| Middle - Zone 2 Temperature | 280 - 295 | °C |
| Rear - Zone 1 Temperature | 265 - 275 | °C |
| Mold Temperature | 80 - 95 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:10/02/2004 | ||