S-Plastics Thermocomp RF006EU resin is a compound based on PA 66 resin containing Glass Fiber. Added features include: Easy Molding,UV-Stabilized
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield, 5 mm/min | 170 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 3.3 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 8800 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 233 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 7600 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | 80 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 14 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| CTE, 23°C to 60°C, flow | 2.4E-05 | 1/°C | ISO 11359-2 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 215 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage, flow (5) | 0.2 | % | S-Plastics Method |
| Density | 1.36 | g/cm³ | ISO 1183 |
| Water Absorption, 23°C/24hrs | 3 | % | ISO 62-1 |
| Source GMD, last updated:2010/01/28 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.15 - 0.25 | % |
| Melt Temperature | 280 - 305 | °C |
| Front - Zone 3 Temperature | 295 - 305 | °C |
| Middle - Zone 2 Temperature | 280 - 295 | °C |
| Rear - Zone 1 Temperature | 265 - 275 | °C |
| Mold Temperature | 95 - 110 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:2010/01/28 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |