S-Plastics Thermocomp PFB42EU resin is a compound based on PA 6 resin containing Glass Fiber, Glass Bead. Added features include Easy
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break, 5 mm/min | 93 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2.6 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 5700 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 145 | MPa | ISO 178 |
| Flexural Stress, break, 2 mm/min | 145 | MPa | ISO 178 |
| Flexural Strain, break, 2 mm/min | 4.4 | % | ISO 178 |
| Flexural Modulus, 2 mm/min | 4700 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | 20 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| CTE, 23°C to 60°C, flow | 4.9E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, xflow | 9.3E-05 | 1/°C | ISO 11359-2 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 156 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage, flow | 0.44 | % | S-Plastics Method |
| Density | 1.35 | g/cm³ | ISO 1183 |
| Water Absorption, 23°C/24hrs | 1.9 | % | ISO 62-1 |
| Source GMD, last updated:10/23/2008 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.15 - 0.25 | % |
| Melt Temperature | 265 - 275 | °C |
| Front - Zone 3 Temperature | 275 - 290 | °C |
| Middle - Zone 2 Temperature | 265 - 275 | °C |
| Rear - Zone 1 Temperature | 250 - 260 | °C |
| Mold Temperature | 80 - 95 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:10/23/2008 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Thermocomp PFB42EU.pdf |
|