S-Plastics Thermocomp RF006XXZ resin is a compound based on Nylon 66 resin containing Glass Fiber.This product is also known as
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break | 165 | MPa | ASTM D 638 |
| Tensile Strain, break | 2.4 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 10680 | MPa | ASTM D 638 |
| Flexural Stress | 235 | MPa | ASTM D 790 |
| Flexural Modulus | 9440 | MPa | ASTM D 790 |
| Tensile Stress, break | 154 | MPa | ISO 527 |
| Tensile Strain, break | 2.4 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 8980 | MPa | ISO 527 |
| Flexural Stress | 234 | MPa | ISO 178 |
| Flexural Modulus | 9220 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 646 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 58 | J/m | ASTM D 256 |
| Instrumented Impact Energy @ peak, 23°C | 6 | J | ASTM D 3763 |
| Multiaxial Impact | 2 | J | ISO 6603 |
| Izod Impact, unnotched 80*10*4 +23°C | 52 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 7 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 265 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 255 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 3.04E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 7.32E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, flow | 3.04E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 7.32E-05 | 1/°C | ISO 11359-2 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 243 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.4 | g/cm³ | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 0.69 | % | ASTM D 570 |
| Mold Shrinkage, flow, 24 hrs | 0.3 - 0.5 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 1.4 - 1.6 | % | ASTM D 955 |
| Mold Shrinkage, flow, 24 hrs | 0.3 - 0.5 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 1.4 - 1.6 | % | ISO 294 |
| Wear Factor Washer | 75 | 10^-10 in^5-min/ft-lb-hr | ASTM D 3702 Modified |
| Dynamic COF | 0.71 | - | ASTM D 3702 Modified |
| Dynamic COF | 0.71 | - | ASTM D 3702 Modified |
| Static COF | 0.57 | - | ASTM D 3702 Modified |
| Static COF | 0.57 | - | ASTM D 3702 Modified |
| Density | 1.39 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C / 50% RH) | 1.2 | % | ISO 62 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Compliant, 94HB Flame Class Rating (3)(4) | 1.5 | mm | UL 94 by GE |
| Source GMD, last updated:09/11/2008 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.15 - 0.25 | % |
| Melt Temperature | 280 - 305 | °C |
| Front - Zone 3 Temperature | 295 - 305 | °C |
| Middle - Zone 2 Temperature | 280 - 295 | °C |
| Rear - Zone 1 Temperature | 265 - 275 | °C |
| Mold Temperature | 95 - 110 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:09/11/2008 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Thermocomp RF006XXZ.pdf |
|