S-Plastics Thermocomp XF006S resin is a compound based on Amorphous Nylon containing Glass Fiber. Characteristics of this grade are: HeatStabilized.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, brk, Type I, 5 mm/min | 138 | MPa | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 2.6 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 9650 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 209 | MPa | ASTM D 790 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 208 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 9060 | MPa | ASTM D 790 |
| Tensile Stress, break, 5 mm/min | 141 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2.5 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 9020 | MPa | ISO 527 |
| Flexural Stress | 214 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 8910 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 632 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 56 | J/m | ASTM D 256 |
| Multiaxial Impact | 3 | J | ISO 6603 |
| Instrumented Impact Total Energy, 23°C | 11 | J | ASTM D 3763 |
| Izod Impact, unnotched 80*10*4 +23°C | 38 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 142 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 138 | °C | ASTM D 648 |
| CTE, -30°C to 30°C, flow | 4.4E-05 | 1/°C | ASTM D 696 |
| CTE, -30°C to 30°C, xflow | 3.5E-05 | 1/°C | ASTM D 696 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 144 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 137 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.36 | - | ASTM D 792 |
| Density | 1.36 | g/cm³ | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 0.22 | % | ASTM D 570 |
| Mold Shrinkage, flow, 24 hrs (5) | 0 - 0 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs (5) | 0.2 - 0.4 | % | ASTM D 955 |
| Moisture Absorption (23°C / 50% RH) | 0.28 | % | ISO 62 |
| Source GMD, last updated:2010/07/08 | |||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Thermocomp XF006S.pdf |
|