S-Plastics Thermocomp DF008P resin is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material
include: Exceptional Processing.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break | 142 | MPa | ASTM D 638 |
| Tensile Strain, break | 2.3 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 10340 | MPa | ASTM D 638 |
| Tensile Stress, break | 148 | MPa | ISO 527 |
| Tensile Strain, break | 2.3 | % | ISO 527 |
| Flexural Stress | 220 | MPa | ISO 178 |
| Flexural Modulus | 18000 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched 80*10*4 +23°C | 14 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| CTE, -40°C to 40°C, flow | 3.5E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 3.7E-05 | 1/°C | ISO 11359-2 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 138 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.52 | g/cm³ | ASTM D 792 |
| Mold Shrinkage, flow, 24 hrs | 0.26 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.4 | % | ISO 294 |
| Source GMD, last updated:04/26/2005 | |||
| THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES. | |||
| PLEASE CHECK WITH YOUR (LOCAL SALES OFFICE) FOR AVAILABILITY IN YOUR REGION | |||
| (1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294. | |||
| (2) Only typical data for selection purposes. Not to be used for part or tool design. | |||
| (3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions. | |||
| (4) Internal measurements according to UL standards. | |||