S-Plastics Thermocomp DFA-113 resin is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of
this material include: Flame Retardant.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield | 60 | MPa | ASTM D 638 |
| Tensile Stress, break | 54 | MPa | ASTM D 638 |
| Tensile Strain, yield | 4.9 | % | ASTM D 638 |
| Tensile Strain, break | 8.2 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 3590 | MPa | ASTM D 638 |
| Flexural Stress | 107 | MPa | ASTM D 790 |
| Flexural Modulus | 3610 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 1068 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 61 | J/m | ASTM D 256 |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 132 | °C | ASTM D 648 |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.29 | g/cm³ | ASTM D 792 |
| Mold Shrinkage, flow, 24 hrs | 0.3 - 0.5 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 0.3 - 0.4 | % | ASTM D 955 |
| Source GMD, last updated:09/28/2004 | |||
| Injection Molding | Value | Unit | |
| Drying Temperature | 120 | °C | |
| Drying Time | 4 | hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 305 - 325 | °C | |
| Front - Zone 3 Temperature | 320 - 330 | °C | |
| Middle - Zone 2 Temperature | 310 - 320 | °C | |
| Rear - Zone 1 Temperature | 295 - 305 | °C | |
| Mold Temperature | 80 - 110 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm | |
| Source GMD, last updated:09/28/2004 | |||
| THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES. | |||
| PLEASE CHECK WITH YOUR (LOCAL SALES OFFICE) FOR AVAILABILITY IN YOUR REGION | |||
| (1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded |
|||
| samples. All samples tested under ISO test standards are prepared according to ISO 294. | |||
| (2) Only typical data for selection purposes. Not to be used for part or tool design. | |||
| (3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions. | |||
| (4) Internal measurements according to UL standards. | |||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Thermocomp DFA-113.pdf |
|