S-Plastics Thermocomp Lexan_BFL2215 resin is GF 15% filled, high flow Lexan, Non Br,Cl FR system, V-2 @0.75mm, WT and BK color
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 62 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 63 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 2.6 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 3.2 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 4900 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 106 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 4220 | MPa | ASTM D 790 |
| Tensile Stress, yield, 5 mm/min | 62 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 65 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 2.6 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2.6 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 4880 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 112 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 4910 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 94 | J/m | ASTM D 256 |
| Izod Impact, notched, -30°C | 69 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 0 | J | ASTM D 3763 |
| Izod Impact, notched 80*10*4 +23°C | 8 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 7 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 6 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 150 | °C | ASTM D 1525 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 137 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 3.E+01 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 6.4E+01 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, flow | 2.8E+01 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 7.3E+01 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate B/50 | 150 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 153 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 138 | °C | ISO 75/Af |
| Relative Temp Index, Elec | 80 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 80 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 80 | °C | UL 746B |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.3 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.37 - 0.38 | % | S-Plastics Method |
| Melt Flow Rate, 200°C/3.8 kgf | 12.7 | g/10 min | ASTM D 1238 |
| Density | 1.3 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.1 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.1 | % | ISO 62 |
| Melt Volume Rate, MVR at 220°C/5.0 kg | 9 | cm³/10 min | ISO 1133 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Recognized, 94V-2 Flame Class Rating (3) | 0.75 | mm | UL 94 |
| Source GMD, last updated:12/01/2005 | |||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Thermocomp Lexan_BFL2215.pdf |
|