S-Plastics Thermocomp ECF62 resin is a compound based on Polyimide resin containing Glass Fiber, Carbon Fiber. Added features of this
material include: Electrically Conductive.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break | 185 | MPa | ASTM D 638 |
| Tensile Strain, break | 1.5 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 17920 | MPa | ASTM D 638 |
| Flexural Stress | 268 | MPa | ASTM D 790 |
| Flexural Modulus | 15850 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 485 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 69 | J/m | ASTM D 256 |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 212 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 2.52E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 2.34E-05 | 1/°C | ASTM E 831 |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.57 | g/cm³ | ASTM D 792 |
| Mold Shrinkage, flow, 24 hrs | 0.1 - 0.2 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 0.3 - 0.4 | % | ASTM D 955 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | 1.E+10 - 1.E+11 | Ohm-cm | ASTM D 257 |
| Source GMD, last updated:09/24/2008 | |||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 - 150 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.05 | % |
| Melt Temperature | 360 - 365 | °C |
| Front - Zone 3 Temperature | 365 - 375 | °C |
| Middle - Zone 2 Temperature | 355 - 365 | °C |
| Rear - Zone 1 Temperature | 345 - 355 | °C |
| Mold Temperature | 120 - 150 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 60 - 100 | rpm |
| Source GMD, last updated:09/24/2008 | ||
| THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES. | ||
| PLEASE CHECK WITH YOUR (LOCAL SALES OFFICE) FOR AVAILABILITY IN YOUR REGION | ||
| (1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294. |
||
| (2) Only typical data for selection purposes. Not to be used for part or tool design. | ||
| (3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions. | ||
| (4) Internal measurements according to UL standards. | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Thermocomp ECF62.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|