S-Plastics Thermocomp R-1000 HI 620 resin is High Impact Nylon 66 compound containing Impact Modifier.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break | 40 | MPa | ISO 527 |
| Tensile Strain, break | 40 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 1700 | MPa | ISO 527 |
| Flexural Stress | 45 | MPa | ISO 178 |
| Flexural Modulus | 1400 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | 98 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 120 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 45 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage, flow, 24 hrs | 2.3 - 2.5 | % | ISO 294 |
| Density | 1.07 | g/cm³ | ISO 1183 |
| Source GMD, last updated:09/30/2004 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.15 - 0.25 | % |
| Melt Temperature | 265 - 275 | °C |
| Front - Zone 3 Temperature | 260 - 270 | °C |
| Middle - Zone 2 Temperature | 255 - 265 | °C |
| Rear - Zone 1 Temperature | 250 - 260 | °C |
| Mold Temperature | 60 - 100 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:09/30/2004 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Thermocomp R-1000 HI 620.pdf |
|