S-Plastics Thermocomp Valox_EXCP0069 resin is a 50% glass reinforced PBT injection moulding resin.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break, 5 mm/min | 145 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 1.5 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 16000 | MPa | ISO 527 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched 80*10*4 +23°C | 10 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 8 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate B/120 | 218 | °C | ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 220 | °C | ISO 75/Be |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 215 | °C | ISO 75/Ae |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.72 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 250°C/2.16 kg | 8 | cm³/10 min | ISO 1133 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Compliant, 94HB Flame Class Rating (3)(4) | 1.6 | mm | UL 94 by GE |
| Source GMD, last updated:07/12/2001 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 110 - 120 | °C |
| Drying Time | 2 - 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 250 - 270 | °C |
| Nozzle Temperature | 240 - 260 | °C |
| Front - Zone 3 Temperature | 245 - 265 | °C |
| Middle - Zone 2 Temperature | 240 - 255 | °C |
| Rear - Zone 1 Temperature | 230 - 245 | °C |
| Hopper Temperature | 40 - 60 | °C |
| Mold Temperature | 40 - 100 | °C |
| Source GMD, last updated:07/12/2001 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |