S-Plastics Thermocomp WH0270FX_WH5A289 resin is 2.7 specific gravity PBT
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 31 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 31 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 0.5 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 0.7 | % | ASTM D 638 |
| Flexural Stress, yield, 2 mm/min | 52 | MPa | ISO 178 |
| Flexural Strain, break, 2 mm/min | 0.8 | % | ISO 178 |
| Flexural Modulus, 2 mm/min | 8320 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 150 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 19 | J/m | ASTM D 256 |
| Izod Impact, unnotched 80*10*4 +23°C | 10 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 3 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 164 | °C | ASTM D 648 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 162 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 2.695 | g/cm³ | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 0.08 | % | ASTM D 570 |
| Mold Shrinkage, flow, 24 hrs | 0.69 - 0.89 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 1 - 1.2 | % | ASTM D 955 |
| Source GMD, last updated:08/13/2008 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.05 | % |
| Melt Temperature | 240 - 265 | °C |
| Front - Zone 3 Temperature | 260 - 270 | °C |
| Middle - Zone 2 Temperature | 245 - 255 | °C |
| Rear - Zone 1 Temperature | 220 - 230 | °C |
| Mold Temperature | 80 - 100 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:08/13/2008 | ||