S-Plastics Thermocomp DF0069E resin is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break | 114 | MPa | ASTM D 638 |
| Tensile Strain, break | 6.8 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 14470 | MPa | ASTM D 638 |
| Flexural Stress | 172 | MPa | ASTM D 790 |
| Flexural Modulus | 7580 | MPa | ASTM D 790 |
| Tensile Stress, break | 120 | MPa | ISO 527 |
| Tensile Strain, break | 7 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 11180 | MPa | ISO 527 |
| Flexural Stress | 183 | MPa | ISO 178 |
| Flexural Modulus | 8800 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 843 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 138 | J/m | ASTM D 256 |
| Izod Impact, unnotched 80*10*4 +23°C | 53 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 14 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 143 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 142 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 5.04E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 3.06E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, flow | 5.1E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 3.1E-05 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 148 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 144 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.47 | g/cm³ | ASTM D 792 |
| Mold Shrinkage, flow, 24 hrs | 0.1 - 0.3 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 0.6 - 0.8 | % | ASTM D 955 |
| Mold Shrinkage, flow, 24 hrs | 0.18 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.69 | % | ISO 294 |
| Density | 1.47 | g/cm³ | ISO 1183 |
| Source GMD, last updated:09/24/2008 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 305 - 325 | °C |
| Front - Zone 3 Temperature | 320 - 330 | °C |
| Middle - Zone 2 Temperature | 310 - 320 | °C |
| Rear - Zone 1 Temperature | 295 - 305 | °C |
| Mold Temperature | 80 - 110 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:09/24/2008 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Thermocomp DF0069E.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|