S-Plastics Cycoloy C1110HF resin is High impact and ductility at 73F and -20F. For thin-wall applications.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 59 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min | 5 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 75 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2200 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 86 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2370 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 640 | J/m | ASTM D 256 |
| Izod Impact, notched, -30°C | 267 | J/m | ASTM D 256 |
| Instrumented Impact Energy @ peak, 23°C | 61 | J | ASTM D 3763 |
| Instrumented Impact Energy @ peak, -30 | 47 | J | ASTM D 3763 |
| Instrumented Impact Total Energy, 23°C | 61 | J | ASTM D 3763 |
| Instrumented Impact Total Energy, -30°C | 54 | J | ASTM D 3763 |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 126 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 110 | °C | ASTM D 648 |
| CTE, -30°C to 30°C, flow | 7.2E-05 | 1/°C | ASTM D 696 |
| Relative Temp Index, Elec | 60 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 60 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 60 | °C | UL 746B |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.14 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.5 - 0.7 | % | S-Plastics Method |
| Melt Flow Rate, 260°C/3.8 kgf | 12 | g/10 min | ASTM D 1238 |
| ELECTRICAL | Value | Unit | Standard |
| Arc Resistance, Tungsten {PLC} | 5 | PLC Code | ASTM D 495 |
| Hot Wire Ignition {PLC) | 3 | PLC Code | UL 746A |
| High Voltage Arc Track Rate {PLC} | 1 | PLC Code | UL 746A |
| High Ampere Arc Ign, surface {PLC} | 0 | PLC Code | UL 746A |
| Comparative Tracking Index (UL) {PLC} | 3 | PLC Code | UL 746A |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Recognized, 94HB Flame Class Rating (3) | 1.21 | mm | UL 94 |
| CSA (See File for complete listing) | LS88480 | File No. | CSA LISTED |
| UV-light, water exposure/immersion | F2 | - | UL 746C |
| Source GMD, last updated:01/05/2000 | |||
| Injection Molding | Value | Unit |
| Drying Temperature | 105 - 110 | °C |
| Drying Time | 3 - 4 | hrs |
| Drying Time (Cumulative) | 8 | hrs |
| Maximum Moisture Content | 0.04 | % |
| Melt Temperature | 275 - 300 | °C |
| Nozzle Temperature | 275 - 300 | °C |
| Front - Zone 3 Temperature | 260 - 300 | °C |
| Middle - Zone 2 Temperature | 255 - 295 | °C |
| Rear - Zone 1 Temperature | 250 - 290 | °C |
| Mold Temperature | 60 - 90 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 40 - 70 | rpm |
| Shot to Cylinder Size | 30 - 80 | % |
| Vent Depth | 0.038 - 0.076 | mm |
| Source GMD, last updated:01/05/2000 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics cycoloy C1110HF.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|