S-Plastics Valox EXVX1310 resin is 35% Glassfiber / Mineral Filled PET, Mold Release, Heat Stabilized
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield, 5 mm/min | 145 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 145 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 1.9 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 1.9 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 12500 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 200 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 9200 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | 40 | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -30°C | 35 | kJ/m² | ISO 180/1U |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 6 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| CTE, 23°C to 80°C, flow | 2.E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 80°C, xflow | 8.E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate B/50 | 235 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 234 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 200 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.6 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.25 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.05 | % | ISO 62 |
| Melt Volume Rate, MVR at 265°C/2.16 kg | 9 | cm³/10 min | ISO 1133 |
| Melt Viscosity, 280°C, 1500 sec-1 | 60 | Pa-s | ISO 11443 |
| Source GMD, last updated:12/21/2007 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 - 130 | °C |
| Drying Time | 4 - 6 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 270 - 290 | °C |
| Nozzle Temperature | 260 - 280 | °C |
| Front - Zone 3 Temperature | 270 - 290 | °C |
| Middle - Zone 2 Temperature | 260 - 280 | °C |
| Rear - Zone 1 Temperature | 250 - 270 | °C |
| Hopper Temperature | 40 - 60 | °C |
| Mold Temperature | 90 - 120 | °C |
| Source GMD, last updated:12/21/2007 | ||
|
For more information please download the datasheet |
|
 |