S-Plastics Valox EXVX1311 resin is Non-Brominated & Non-Chlorinated Flame Retardant, 30% Glass fiber reinforced PBT/PET blend
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield, 5 mm/min | 95 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 95 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 1.5 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 1.5 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 8500 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 150 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 10000 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | 30 | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -30°C | 25 | kJ/m² | ISO 180/1U |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/120 | 190 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 190 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.6 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 265°C/5.0 kg | 25 | cm³/10 min | ISO 1133 |
| ELECTRICAL | Value | Unit | Standard |
| Comparative Tracking Index | 400 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Compliant, 94V-0 Flame Class Rating (3)(4) | 1.5 | mm | UL 94 by GE |
| Glow Wire Flammability Index 960°C, passes at | 3 | mm | IEC 60695-2-12 |
| Glow Wire Ignitability Temperature, 3.0 mm | 800 | °C | IEC 60695-2-13 |
| Source GMD, last updated:11/09/2007 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 110 - 120 | °C |
| Drying Time | 4 - 6 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 260 - 285 | °C |
| Nozzle Temperature | 265 - 275 | °C |
| Front - Zone 3 Temperature | 260 - 280 | °C |
| Middle - Zone 2 Temperature | 255 - 280 | °C |
| Rear - Zone 1 Temperature | 240 - 260 | °C |
| Hopper Temperature | 40 - 60 | °C |
| Mold Temperature | 60 - 110 | °C |
| Source GMD, last updated:11/09/2007 | ||
|
For more information please download the datasheet |
|
 |
S-Plastics Valox EXVX1311.pdf |
|